In the Y-Ba-Cu-O system YBa2Cu3Ox phase is produced by the following peritectic reaction: Y2BaCuO5 + liquid yields 2YBa2Cu3Ox. Through the control of processing conditions and starting compositions it becomes possible to fabricate large crystals containing fine Y2BaCuO5(211) inclusions. Such crystals exhibit Jc values exceeding 10000 A/sq cm at 77 K and 1T. Recently, researchers developed a novel process which can control the volume fraction of 211 inclusions. Elimination of 211 inclusions is also possible. In this study, researchers prepared YBaCuO crystals with and without 211 inclusions using the novel process and compared flux pinning, flux creep and critical currents. Magnetic field dependence of Jc for YBaCuO crystals with and without 211 inclusions is shown. It is clear that fine 211 inclusions can contribute to flux pinning. It was also found that flux creep rate could be reduced by increasing flux pinning force. Critical current density estimates based on the conventional flux pinning theory were in good agreement with experimental results.